Nitrile Rubber Sheets

Excellent, resistance to oils, fuels, petroleum, most solvents. Good abrasion resistance. 62 shore A hardness. Tensile strength at break: 5Mpa. Elongation at break: 200%

Para Shotblast Rubber Sheets

Tan coloured natural rubber. Outstanding resistance to wear and abrasion-used as protective screening in shotblasting applications but also used in strip or gasket form where durability is essential. 45 shore A hardness. Tensile strength at break: 15Mpa. Elongation at break: 400%

Shotblast Rubber Sheets

A cost-effective, abrasion-resistant rubber. 62 shore A hardness. Tensile strength at break: 10Mpa. Elongation at break: 350%

Neoprene Rubber Sheets

Good resistance to material oils, greases, dilute acids and alkalis. Good ageing and weathering properties make it suitable for outdoor applications. 65 shore A hardness. Tensile strength at break: 6Mpa. Elongation at break: 250%

Insertion Rubber Sheets

Similar properties to standard commercial but embedded textile reinforcement offers increased tensile strength and tear resistance. 68 shore A hardness. Tensile strength at break: 2.5Mpa. Elongation at break: 200%

Nitrile Rubber Sheets

Excellent, resistance to oils, fuels, petroleum, most solvents. Good abrasion resistance. 62 shore A hardness. Tensile strength at break: 5Mpa. Elongation at break: 200%

Commercial Black Sheets

General-purpose grade for water service and dilute chemicals. Low cost waterproof seals, gaskets. 68 shore A hardness. Tensile strength at break: 3.0Mpa. Elongation at break: 200%.

Food Quality White Rubber Sheets

White, non-marking rubber manufactured FDA approved ingredients. Use in all food and beverage industries or sealing applications. Avoid vegetable/animal oils. 62 shore A hardness. Tensile strength at break: 4Mpa. Elongation at break: 300%

M228 EPDM Rubber Sheets

EPDM RUBBER is ideal for outdoor application because of its excellent resistance to ozone, oxidants and severe weather conditions. 67 shore A hardness. Tensile strength at break: 5Mpa. Elongation at break: 300%

Insertion Rubber

Similar properties to standard commercial but embedded textile reinforcement offers increased tensile strength and tear resistance. 68 shore A hardness.
Tensile strength at break: 2.5 Mpa. Elongation at break: 200%