Cast Iron Electrodes S-NFC

A Graphite coated Iron-Nickel alloy electrode for high strength jointing of cast iron and cold welding of cast iron, it deposits 95%Ni + 2%Fe weld metal.
Can be used for repairing broken cast iron, joining of cast iron to steel and building up worn parts.
Meets the following standards:
AWS A 5.15 E Ni-C1
Din 8573 E Ni BG 11

2.5mm

Recommended Amperage: 70A

Stainless Steel Mig Wire

Ideal for welding stainless steels. It has increased silicon content for an improved weld that produces a smoother more consistent bead making it ideal for use were appearance is important. For use on stainless steel structures. Supplied on a precision layer wound reel for positive uninterupted feeding. Weight: 15kg.

Stainless Steel Mig Wire

Ideal for welding stainless steels. It has increased silicon content for an improved weld that produces a smoother more consistent bead making it ideal for use were appearance is important. For use on stainless steel structures. Supplied on a precision layer wound reel for positive uninterupted feeding. Weight: 15kg.

Electrodes for Mild Steels

Available in 2.6 x 300mm, 3.2mm x 350mm and 4mm x 400mm.

E7018 (?Low Hydrogen?)

Basic coated, all positional rods.
Applications: for steel plate structural steels, pipe work and forgings. Ideal for repairs of casting and machinery, compensate for dilution effect of poor steels. Often used where rutile deposits may be at risk from cracking.
N.B. Suitable for AC (70V minimum open circuit) and DC. Optimum rooting operability is obtained using DC-.
Recommended Amperages;
Size(mm) 2.5 3.2 4.0.
Min. 70A 95A 130A.
Max. 100A 125A 170A.

Sainless Steel Electrode S316L

A Lime-Titania electrode giving excellent useability and weldability, it deposits 19.5%Cr - 11.7%Ni - 2.5%Mo weld metal.
The Austenite structure gives good crack resisting properties. For welding of extra-low carbon 18%Cr-12Ni-Mo stainless steel.

Sterrod+ S316L 1.6mm Electrodes