The heat and surface treatment plus the high quality of steel used in the manufacturing process ensure the springs will bear a high number of stresses without breaking or without appreciable loss of load. Every batch of springs is subject to a rigorous testing procedure to ensure that a consistent quality is maintained. Longer springs should be guided along their course.

Extra Heavy-Load Springs Colour Coded Yellow

Heavy Duty CNC Tool Storage Trolley

This heavy duty trolley allows tools to be transported safely and effectively throughout a workshop environment.
The trolley will accept up to 24 tool blocks, dependent upon tooling size.
Dimensions (H x W x D): 1150 x 1115 x 600mm.
Tool block capacity: 24

Bott Drawer Divider Kits - Medium Duty

Customise your storage system with a high quality range of drawer division accessories.



For drawers 500 x 550mm (W x D)

6 Compartment

Indexa Die Springs

The heat and surface treatment plus the high quality of steel used in the manufacturing process ensure the springs will bear a high number of stresses without breaking or without appreciable loss of load. Every batch of springs is subject to a rigorous testing procedure to ensure that a consistent quality is maintained. Longer springs should be guided along their course.

Medium Load Springs Colour-Coded Blue

Precision Ground Flat Stock (500mm)

The dimensional stability of ground flat stock combines with other useful characteristics including excellent resistance to cracking during heat treatment compared with other, more highly alloyed, cold work tools. Relatively soft and easy to machine. High wear resistance after heat treatment. Holds a good cutting edge. Suitable for EDM machining.
Typical applications: widely used in precision tools, machine knives, gauges, jigs, templates, punches, dies and machine parts.
The Cost Cutting Stock: extensive range of widths and thicknesses enables the selection of an appropriate size of ground flat stock to minimise material and machining costs.

Manufactured from BS4659 B01 grade steel equivalent to AISI 01 and Werk. No. 1.2510.
Chemical analysis range:
Carbon 0.90 - 1.00%
Silicon 0.40%
Manganese 1.00 - 1.20%
Chromium 0.50 - 0.70%
Tungsten 0.50 - 0.70%
Vanadium 0.05 - 0.25%

Chemical analysis typical:
Carbon 0.95%
Silicon 0.40%
Manganese 1.20%
Chromium 0.55%
Tungsten 0.55%
Vanadium 0.15%

Metric sizes

Tolerances:
Thickness: -0.00mm/+0.050mm.
Width: -0.00mm/+0.200mm.
Length: -0.00mm/+5.000mm.

Silver Steel

For tool room and general engineering. Applications include screwdrivers, punches, shafts, axles, pinions, pins, die posts, instrument parts, model parts, taps and drills for mild steel, engraver tools. High carbon content means that it can be hardened to give high wear resistance and chromium content adds strength and hardness.

Manufactured from
BS1407:1970 grade steel.

Typical hardness:
207-237HB with 285HB maximum.

Tensile strength:
45/55 T.P.S.I. (700/850 N/mm2).

Surface finish:
Better than 0.6 microns (25 micro inch) CLA (Centre Line Average).

Chemical analysis range:
Carbon 0.95 - 1.25%
Silicon 0.40% max
Manganese 0.25 - 0.45%
Phosphorous 0.045% max
Sulphur 0.045% max
Chromium 0.35 - 0.45%

Chemical analysis typical:
Carbon 1.13%
Silicon 0.22%
Manganese 0.37%
Phosphorous 0.014%
Sulphur 0.018%
Chromium 0.43%

Inch round sizes

Tolerances:
Below 1" plus/minus 0.00025".
1" up to and including 2" plus/minus 0.00050".

Silver Steel

For tool room and general engineering. Applications include screwdrivers, punches, shafts, axles, pinions, pins, die posts, instrument parts, model parts, taps and drills for mild steel, engraver tools. High carbon content means that it can be hardened to give high wear resistance and chromium content adds strength and hardness.

Manufactured from
BS1407:1970 grade steel.

Typical hardness:
207-237HB with 285HB maximum.

Tensile strength:
45/55 T.P.S.I. (700/850 N/mm2).

Surface finish:
Better than 0.6 microns (25 micro inch) CLA (Centre Line Average).

Chemical analysis range:
Carbon 0.95 - 1.25%
Silicon 0.40% max
Manganese 0.25 - 0.45%
Phosphorous 0.045% max
Sulphur 0.045% max
Chromium 0.35 - 0.45%

Chemical analysis typical:
Carbon 1.13%
Silicon 0.22%
Manganese 0.37%
Phosphorous 0.014%
Sulphur 0.018%
Chromium 0.43%

Metric round sizes

Tolerances:
Up to 25mm plus 0 - 0.012mm.
Over 25mm up to and including 50mm plus 0 - 0.0250mm.

Kennedy® Heavy-Duty Industrial Keyed Drill Chuck

Fully hardened and ground working parts. The jaws are centre ground for alignment and concentricity. Keyholes and teeth are fully hardened for durability and wear resistance. To correctly tighten your keyed drill chuck use all key holes in turn to guarantee even pressure and maximum grip. Suitable for use on machine tools and all types of industrial power tools. Supplied with key. Manufactured to DIN 6349.

Engineers Workbenches

Available with the following worktop finishes.
Wisa - Laminated ply core with mid grey polypropylene face. An easy clean top with good resistance to oil, grease, mild alkalis and weak acids.
Mfc - Particle board core with light grey laminate face. A light duty easy clean top suitable for assembly or office environments.
Mpx - Laminated beech ply. A tough, general duty top suitable for most applications.

Pedestal bench

For optimum access and flexibility each pedestal bench leg is adjustable, giving height adjustment from 780 - 930mm.
The 30mm worktop is available in multiplex or wisa.

Toolholders for Quick Change Toolposts

Ideal for all machine shop use.

Standard Type